THÀNH PHẦN HÓA HỌC THÉP KHÔNG gỉ
|
Mác thép
|
Carbon
(C)
|
Mangan
(Mn)
|
Phốt pho
(P)
|
Lưu huỳnh
(S)
|
Silic
(Si)
|
Chrom
(Cr)
|
Niken
(Ni)
|
Molybden
(Mo)
|
Các nguyên tố khác
|
201
|
0.15max
|
5.50
7.50
|
0.060
|
0.030
|
1.00
|
16.00
18.00
|
3.50
5.50
|
–
|
N
0.25
|
202
|
0.15max
|
7.50
10.00
|
0.060
|
0.030
|
1.00
|
17.00
19.00
|
4.00
6.00
|
–
|
N
0.25
|
|
|
|
|
|
|
|
|
|
|
301
|
0.15max
|
.00
|
0.045
|
0.030
|
1.00
|
16.00
18.00
|
6.00
8.00
|
–
|
–
|
302
|
0.15max
|
2.00
|
0.045
|
0.030
|
1.00
|
17.00
19.00
|
8.00
10.00
|
–
|
–
|
302 B
|
0.15max
|
2.00
|
0.045
|
0.030
|
2.00
3.00
|
17.00
19.00
|
8.00
10.00
|
–
|
–
|
303
|
0.15max
|
2.00
|
0.20
|
Min
0.15
|
1.00
|
17.00
19.00
|
8.00
10.00
|
0.60
|
Zr
0.60
|
303 Se
|
0.15max
|
2.00
|
0.20
|
0.06
|
1.00
|
17.00
19.00
|
8.00
10.00
|
–
|
–
|
304
|
0.08max
|
2.00
|
0.045
|
0.030
|
1.00
|
17.00
19.00
|
8.00
10.00
|
–
|
–
|
304 L
|
0.03Max
|
2.00
|
0.045
|
0.030
|
1.00
|
18.00
20.00
|
8.00
12.00
|
–
|
–
|
305
|
0.12max
|
2.00
|
0.045
|
0.030
|
1.00
|
17.00
19.00
|
8.00
10.00
|
–
|
–
|
308
|
0.08max
|
2.00
|
0.045
|
0.030
|
1.00
|
17.00
19.00
|
8.00-10.00
|
–
|
–
|
309
|
0.20max
|
2.00
|
0.045
|
0.030
|
1.00
|
22.00
24.00
|
12.00
5.00
|
–
|
–
|
309 S
|
0.08Max
|
2.00
|
0.045
|
0.030
|
1.00
|
22.00
24.00
|
12.00
5.00
|
–
|
–
|
310
|
0.25max
|
2.00
|
0.045
|
0.030
|
1.50
|
24.00
26.00
|
19.00
22.00
|
–
|
–
|
310 S
|
0.08max
|
2.00
|
0.045
|
0.030
|
1.50
|
24.00
26.00
|
19.00
22.00
|
–
|
–
|
314
|
0.25Max
|
2.00
|
0.045
|
0.030
|
1.50
|
17.00
19.00
|
8.00
10.00
|
–
|
–
|
316
|
0.08max
|
2.00
|
0.045
|
0.030
|
1.00
|
16.00
18.00
|
10.00
14.00
|
2.00
3.00
|
–
|
316 L
|
0.03max
|
2.00
|
0.045
|
0.030
|
1.00
|
16.00
18.00
|
10.00
14.00
|
2.00
3.00
|
–
|
317
|
0.08max
|
2.00
|
0.045
|
0.030
|
1.00
|
18.00
20.00
|
11.00
15.00
|
3.00
4.00
|
–
|
321
|
0.08max
|
2.00
|
0.045
|
0.030
|
1.00
|
17.00
18.00
|
8.00
12.00
|
–
|
Ti
5xC
|
347
|
0.08max
|
2.00
|
0.045
|
0.030
|
2.00
3.00
|
17.00
18.00
|
9.00
13.00
|
–
|
Ta
10xC
|
348
|
0.08max
|
2.00
|
0.045
|
0.030
|
2.00
3.00
|
17.00
19.00
|
9.00
13.00
|
–
|
Cb-Ta | Ta
10xC | 0.10
|
|
|
|
|
|
|
|
|
|
|
403
|
0.08max
|
2.00
|
0.045
|
0.030
|
0.50
|
11.50
13.00
|
–
|
–
|
–
|
405
|
0.08max
|
2.00
|
0.045
|
0.030
|
1.00
|
11.50
14.50
|
–
|
–
|
–
|
410
|
0.15max
|
1.00
|
0.040
|
0.030
|
1.00
|
11.50
13.50
|
–
|
–
|
–
|
414
|
0.15max
|
1.00
|
0.040
|
0.030
|
1.00
|
11.50
13.50
|
1.25
2.50
|
–
|
–
|
416
|
0.15max
|
1.25
|
0.06
|
0.15 min
|
1.00
|
12.00
14.00
|
–
|
0.60
|
–
|
416 Se
|
0.15max
|
1.25
|
0.06
|
0.15 min
|
1.00
|
12.00
14.00
|
–
|
–
|
Se
0.15 Min
|
420
|
> 0.15
|
1.00
|
0.040
|
0.030
|
1.00
|
12.00
14.00
|
–
|
–
|
–
|
430
|
0.12max
|
1.00
|
0.045
|
0.030
|
1.00
|
14.00
18.00
|
–
|
–
|
–
|
430F
|
0.12max
|
1.25
|
0.06
|
0.15 min
|
1.00
|
14.00
18.00
|
–
|
0.60
|
–
|
430F Se
|
0.12max
|
1.25
|
0.06
|
0.06
|
1.00
|
14.00
18.00
|
–
|
–
|
Se
0.15 Min
|
431
|
0.20max
|
1.00
|
0.045
|
0.030
|
1.00
|
15.00
17.00
|
1.25
2.50
|
–
|
–
|
440A
|
0.60
0.75
|
1.00
|
0.040
|
0.030
|
1.00
|
16.00
18.00
|
–
|
0.75
Max
|
–
|
440B
|
0.75
0.95
|
1.00
|
0.040
|
0.030
|
1.00
|
16.00
18.00
|
–
|
0.75
Max
|
–
|
440-C
|
0.95
1.20
|
1.00
|
0.040
|
0.030
|
1.00
|
16.00
18.00
|
–
|
0.75
Max
|
–
|
440XH
|
1.60
|
0.50
|
–
|
–
|
0.40
|
16.00
|
0.35
|
0.80
|
–
|
446
|
0.20max
|
1.50
|
0.040
|
0.030
|
1.00
|
23.00
27.00
|
–
|
–
|
N
0.25max
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
501
|
0.10max
|
1.00
|
0.040
|
0.030
|
1.00
|
4.00
6.00
|
–
|
0.40
0.65
|
–
|
502
|
> 0.10
|
1.00
|
0.040
|
0.030
|
1.00
|
4.00
6.00
|
–
|
0.40
0.65
|
–
|
|
|
|
|
|
|
|
|
|